Ceramics based on alumina is increasingly being used due to their unique properties - high strength, hardness, wear and chemical resistance - as mills lining (liner) and material for the manufacture of grinding elements (grinding media) - balls and cylinders (cylpebs). The use of such liners improves the grinding process effectiveness and prevents size reduction of the metal on the inner surface of the drum mill.

  • Kiln furniture - low saggers
  • Kiln furniture – saggers
  • Chamotte goods - ledge NT
  • Tube MSC with one end closed - thermocouple protection tube
  • Tube MSC for production and repair of thermocouples
  • Tube MSC
  • Boat (tray)

Refractory ceramics, manufactured by the company include mullite-siliceous ceramics in accordance with Data Sheet 26.2-33273315-001: 2005 "mullite-siliceous products", as well as fire clay products manufactured in accordance with the drawings, approved by the customer.

Physical and chemical properties of mullite-siliceous ceramics products:

Mass fraction, % Rate
Al2O3, % - Not less than 52
Fe2O3, % - Not more than 0,7
Refractoriness, °С - Not less than 1750
Water absorption, % - Not more than 0,2
Thermal stability, the number of thermal cycles - Not less than 3
Recommended operating temperature, °С - 1350


Refractory chamotte, small-size goods with complex configuration and weight of not more than 2 kg, with refractoriness of at least 1600 °C are used in electric heating devices and various thermal units. The products are manufactured according to the drawings, agreed with the customer.

The products have the following characteristics:

Grade Al2O3, % Refractoriness, °С Open porosity, % Compressive resistance, N/mm2 Temperature of Softening start, °С
ChA 30 1750 24 20 1300
ChB 28 1650 24 - -

  • Bushing for small oil-immersed transformers
  • Cordierite insulators
  • Beads for heating elements
  • Terminal blocks
  • Spacers for reactors

It is widely used for manufacture of dielectric, semiconductor, piezoelectric, magnetic and ceramic-metal products.

In some cases, ceramic, mainly electroporcelain goods are glazed, which reduces the possibility of contamination, improves electrical and mechanical properties, as well as the appearance of the product.

Electrotechnical porcelain

The basic ceramic material, which is used for manufacture of low-voltage and high-voltage insulators and other insulating elements with operating voltage up to 1150 kV AC and up to 1500 kV DC, is resistant to leakage current, non-flammable, and completely resistant to temperatures up to 1000 ° C.

It is used for manufacturing of cartridges and sockets for the lighting industry, housing cover of high-voltage insulators, insulators for power and electrical engineering, as well as in electrothermics for production of terminal blocks, and many other goods.

Physical properties

C 110 C 111
open porosity % 0 3
density g / cm3 2.2 2.2
flexural strength (non glazed material) N / mm3 50 40
elasticity modulus GPa 80 110
linear elongation coefficient
20...100°С 10-6 K-1
20...600°С 10-6 K-1
thermal conductivity 20...100°С W/m•K 1...2.5 1...2.5
temperature for resistance of 1 MΩ • cm, min. °С 350 350



It is produced in accordance with GOST (National Stat Standard) 20419-83 "Electrical Ceramic. Classification and technical requirements ", group 700, subgroup 780.

Ultraporcelain products are used:
- in radio and electrical engineering, as a material suitable for the manufacture of installation products and low-value capacitors.

Cordierite ceramics

We make products for equipment of high and low voltages. Cordierite grade K-2 groups II, III is used for production of insulators for interruption chambers, magnetic switches, contactors, controllers, rheostats, electric furnaces and other electric heating appliances which work at DC and AC of up to 50 Hz and 60 Hz.

Nominal operating voltage of low voltage insulators is less than 500 V, of high voltage ones is less than 10 kV.

It is used at ambient temperature from minus 50 to plus 800 ° C, relative air humidity of 80% at a temperature of 20 + 5 ° C; ambient temperature plus 1100 ° C.

Steatite ceramics

Steatite ceramic goods and materials used as insulators in high-voltage and high-frequency engineering are made on the basis of the steatite mineral (a kind of talc). SC is characterized by considerable strength in static bending - up to 190 Mn / m2 (1900 kgf / cm2), the dielectric constant is in the range 5.5-7, dielectric loss (at a frequency of 1 MHz and 20 ° C) (3 25) 4.10

Main areas of application of our products are mechanical engineering, chemical and electroheat industries, sanitary and medical equipment.

It is produced in accordance with GOST (National State Standard) 20419-83 "Electrical Ceramics. Classification and technical requirements ", group 200, subgroups 210, 220, 220.1.

C 210 C 220 C 220.1
open porosity % - - -
density g / cm3 2.8 - 2.8
flexural strength (non glazed material) N / mm3 90 120 120
Elasticity modulus MPa 60 80 80
thermal conductivity 20...100 °С Вт/м K 1...2.5 2...3 2...3
Specific insulation resistance at constant current, Ohm * cm, not less than, at the temperature 20…200…600 °С -…1010…104 1013…1010…105 1013…1010…105